In situ synthesis of Al2O3–SiC powders via molten-salt-assisted aluminum/carbothermal reduction method

Al₂O₃–SiC composite powder (ASCP) was successfully synthesized using a novel molten-salt-assisted aluminum/carbothermal reduction (MS-ACTR) method with silica fume, aluminum powder, and carbon black as raw materials; NaCl–KCl was used as the molten salt medium. The effects of the synthesis temperature and salt-reactant ratio on the phase composition and microstructure were investigated. The results showed that the Al₂O₃–SiC content increased with an increase in molten salt temperature, and the salt–reactant ratio in the range of 1.5:1–2.5:1 had an impact on the fabrication of ASCP. The optimum condition for synthesizing ASCP from NaCl–KCl molten salt consisted of maintaining the temperature at 1573 K for 4 h. The chemical reaction thermodynamics and growth mechanism indicate that the molten salt plays an important role in the formation of SiC whiskers by following the vapor-solid growth mode in the MS-ACTR treatment. This study demonstrates that the addition of molten salt as a reaction medium is a promising approach for synthesizing high-melting-point composite powders at low temperatures.     

射频电缆的幅相稳定性测试研究

对射频电缆幅相稳定性进行了介绍,阐述了射频测试电缆相位和幅度变化的因素,并详细分析了射频电缆相位性能以及幅度性能的不同测试方法,最后通过实测数据的展示,总结说明了在日常测试中该如何正确使用测试电缆。     

核磁共振磷谱法测定乳制品中的酪蛋白含量

基于插值法建立乳制品中酪蛋白的核磁共振磷谱定量检测方法。结果表明，该方法的检出限为0.38 g/L（信噪比（RSN）=3），定量限为1.25 g/L（RSN=10）；在5.00～35.00 g/L质量浓度范围内线性良好，相关系数R2大于0.999；加标回收率在91.94%～105.10%范围区间；日内精密度在0.65%～1.40%范围区间；日间精密度在1.40%～1.80%范围区间。对市售不同乳制品中酪蛋白含量进行检测，该方法与GB 31638—2016《酪蛋白》测定结果误差在±5%以内，满足方法可行性对比分析验证要求。该方法相比常规方法样品前处理简单、定量准确性高，大大缩短了检测时间，且有更广泛的适用性，满足乳制品中酪蛋白快速定量检测的要求。     

Dielectric breakdown behavior of ferroelectric ceramics: The role of pores

Dielectric breakdown is a fundamental issue for ferroelectric ceramics. In this work, a phase-field method is introduced to study the breakdown behavior of ferroelectric ceramics with pores randomly distributed. Effects of the position and the size of pores on the breakdown behavior are analyzed. Results indicate that the position of pores, for example in grains or at grain boundaries, has a significant influence on the breakdown strength of ferroelectric ceramics. The nominal breakdown strength of ferroelectric ceramics with 2 % pores at grain boundaries is almost 50 % higher than 2 % pores in grains. Further, for ferroelectric ceramics with a certain porosity, the smaller the pore size, the higher the breakdown strength. As the nominal pore size decreases from 2.5 to 1, the nominal breakdown strength is enhanced from 0.73 to 1.16. Such results agree well with the widely accepted Gerson-Marshall model and previously published experimental observations.     

The spheroidization process of micron-scaled α-Al2O3 powder in hydrothermal method

Understanding the spheroidization process of micron-scaled α-Al₂O₃ powder in hydrothermal method is of great importance but still not completely revealed. The results demonstrated that SO₄^2? played a significant role in the formation of spherical powder, while the bubble generated from the reaction of urea didn't work in the spheroidization process. The spheroidization process was summed up as two steps. The first was that SO₄^2? limited the hydrolysis of Al³⁺ and reacted with Al³⁺ and OH^- to form Al₄(OH)₁₀SO₄, which nucleated and agglomerated into granular precipitates. The second was Ostwald ripening, which gave the spherical precursors a double-layered structure. When the spherical precursors obtained 120 °C were sintered at 1200 °C, α-Al₂O₃ were got and the spherical morphology still maintained with a large number of nano-sized pores. We anticipate the spherical α-Al₂O₃ with nano-sized pores can be applied in adsorption and filtration industries.     

Warpage control method during surface forming process of plastic film-reinforced flexible decorative veneer

The plastic film of the new plastic film reinforced pliable decorative veneer (PRPDSV) is used as a flexible reinforcement material and an adhesive material. It has good water resistance, impermeability, simple preparation and finishing processes, and no formaldehyde release. However, warpage phenomenon during hot pressing has been a bottleneck problem restricting its industrial development. In order to solve this problem solve, the study proposed a concave, and convex molds method, established an elastic–plastic FEA model of hot pressing processes of the PRPDSV using concave and convex molds with static/general static solution module in the nonlinear ABAQUS, and researched the effect on the performances of the PRPDSV from the parameters of temperature, pressure, and mold curvature radius theoretically and verified experimentally. Analysis results showed that the surface forming temperature had a great effect on warpage control for PRPDSV. The higher the temperature is, the smaller the curvature radius of the corresponding mold will be and the better the warpage will be. The curvature radius of the molds had a significant effect on the warpage control. Under the conditions with the same hot pressing parameters, the smaller the curvature radius is, and the better control on the warpage for the PRPDSV will be.     

Numerical Investigation of the Capture of Polydisperse Particles by Charged Droplets

The capture of particles by charged droplets was simulated by considering the electrostatic interactions of droplet-droplet and droplet-particle. The results indicate that the electrostatic repulsion between droplets leads to a dynamic accumulation mode of particles. However, the droplet spacing has an insignificant effect on the capture efficiency when the electrostatic deposition predominates. The increase of droplet charge remarkably improves the capture efficiency, in which the capture of fine particles accounts for the largest proportion. Compared to the droplet charge, the droplet size shows a limited improvement in the capture efficiency. Reducing the droplet velocity prolongs the capture time instead of enhancing the capture capacity per unit time, thereby improving capture efficiency.     

Influence of Sm and Cd co-substitutions on physical,magnetic, Mössbauer,electric, and dielectric properties of Co2X hexagonal ferrites in presence of a hematite phase

X-type samarium-cadmium co-substituted hexaferrite with compositions Ba_2-xSm_xCo₂Cd_yFe_28-yO₄₆ (0.00 ≤ x ≤ 0.08, and 0 ≤ y ≤ 0.4) were prepared at 1340 °C using a simple heat treatment technique. All heated samples were characterized using FTIR, XRD, SEM, VSM, M?ssbauer, and low-frequency dielectric measurements. XRD analysis of prepared samples shows the formation of X as a major phase along with hematite. The M_S value varied from 67.01 Am²/kg to 50.43 Am²/kg; whereas the H_c value changed from 2.95 kA/m to 6.17 kA/m, A high value of M_S (67.01 Am²/kg) is observed in the pure sample, and a very low value of H_c (2.95 kA/m) is observed for x = 0.06, y = 0.3 compositions, but Mr/Ms < 0.5 confirm the multi-domain nature of prepared hexaferrites. Hysteresis loops of all samples are narrow, and confirmed that formed samples belong to magnetically soft. Mössbauer spectra of the three samples (S1, S3, and S5) show the existence of doublets. Significantly low values of coercivity, retentivity, and loss tangent in Sm–Cd substituted samples signified those prepared materials can be used to design electromagnets, transformer cores, electric motors, and maybe a potential candidate for lossless low-frequency applications.     

A globally convergent BFGS method for pseudo-monotone variational inequality problems

In this paper, we propose a globally convergent BFGS method to solve Variational Inequality Problems (VIPs). In fact, a globalization technique on the basis of the hyperplane projection method is applied to the BFGS method. The technique, which is independent of any merit function, is applicable for pseudo-monotone problems. The proposed method applies the BFGS direction and tries to reduce the distance of iterates to the solution set. This property, called Fejer monotonicity of iterates with respect to the solution set, is the basis of the convergence analysis. The method applied to pseudo-monotone VIP is globally convergent in the sense that subproblems always have unique solutions, and the sequence of iterates converges to a solution to the problem without any regularity assumption. Finally, some numerical simulations are included to evaluate the efficiency of the proposed algorithm.